Second, the nature of the main hardening agent before curing agent 6005A-CR 6005B-CR
Color black dark brown liquid viscosity of liquid 25 ℃ 1.4 × 103cps 50cps
Specific gravity of 1.7 ~ 1.8 1.1 ~ 1.15

Third, the use of
A, B group were accurately weighed according to the standard ratio, stir well before use. Such as when used in a large cast profiles, can be divided into several plastic irrigation completed.
Storage: Place in a cool dark place, can be stored for six months.

Fourth, the use of terms
1, the mixing ratio A: B = 100:20 (weight ratio)
2, mixed viscosity 25 ℃ 3000cps
3, the gel time 25 ℃ × 8-10 hours
4, use the time to 25 ℃ × 2 hours (the amount of mixing 100g)
5, hardening condition 70-80 ℃ × 2 小时

Fifth, the nature of the volume resistivity of cured 25 ℃ Ohm.cm 1.2 × 1015
Surface resistance 25 ℃ Ohm 1.3 × 1014
Voltage resistance 25 ℃ KV/mm2 16 ~ 19
Compressive strength of 25 ℃ Kg/mm2 20 ~ 23
Bending strength of 25 ℃ Kg/mm2 9 ~ 11
Impact Strength 25 ℃ Kg/cm/mm2 6 ~ 9
Rate 1KHZ 3.8 dielectric
Dielectric loss 1KHZ 0.02
Heat distortion temperature of 90 ℃